Organic electroluminescent compound, and organic electroluminescent material and organic electroluminescent device comprising the same

ABSTRACT

The present disclosure relates to an organic electroluminescent compound, and an organic electroluminescent material and an organic electroluminescent device comprising the same. The organic electroluminescent compound of the present disclosure has excellent color purity, solubility, and thermal stability. By comprising the organic electroluminescent compound and the organic electroluminescent material of the present disclosure, an organic electroluminescent device showing low driving voltage, excellent current and power efficiencies, and significantly improved lifespan can be provided.

TECHNICAL FIELD

The present disclosure relates to an organic electroluminescent compound, and an organic electroluminescent material and an organic electroluminescent device comprising the same.

BACKGROUND ART

An electroluminescent (EL) device is a self-light-emitting device which has advantages in that it provides a wider viewing angle, a greater contrast ratio, and a faster response time. An organic EL device was first developed by Eastman Kodak, by using small aromatic diamine molecules and aluminum complexes as materials to form a light-emitting layer [Appl. Phys. Lett. 51, 913, 1987].

The most important factor determining luminous efficiency in the organic EL device is light-emitting materials. Until now, fluorescent materials have been widely used as light-emitting material. However, in view of electroluminescent mechanisms, since phosphorescent materials theoretically enhance luminous efficiency by four (4) times compared to fluorescent materials, phosphorescent light-emitting materials have been widely researched. Iridium(III) complexes have been widely known as phosphorescent materials, including bis(2-(2′-benzothienyl)-pyridinato-N,C-3′)iridium(acetylacetonate) ((acac)Ir(btp)₂), tris(2-phenylpyridine)iridium (Ir(ppy)₃) and bis(4,6-difluorophenylpyridinato-N,C2)picolinate iridium (Firpic) as red-, green-, and blue-emitting materials, respectively.

At present, 4,4′-N,N′-dicarbazol-biphenyl (CBP) is the most widely known host material for phosphorescent materials. Recently, Pioneer (Japan) et al., developed a high performance organic EL device using bathocuproine (BCP) and aluminum(III) bis(2-methyl-8-quinolinate)(4-phenylphenolate) (BAlq), etc., as host materials, which were known as hole blocking materials.

Although these materials provide good luminous characteristics, they have the following disadvantages: (1) Due to their low glass transition temperature and poor thermal stability, their degradation may occur during a high-temperature deposition process in a vacuum. (2) The power efficiency of the organic EL device is given by [(π/voltage)×current efficiency], and the power efficiency is inversely proportional to the voltage. Although the organic EL device comprising phosphorescent host materials provides higher current efficiency (cd/A) than one comprising fluorescent materials, a significantly high driving voltage is necessary. Thus, there is no merit in terms of power efficiency (Im/W). (3) Furthermore, the operational lifespan of the organic EL device is short, and luminous efficiency is still required to be improved.

Korean Patent Application Laying-open No. 10-2010-0108924 and Korean Patent Application Laying-open No. 10-2014-0015259 disclose a compound having a dibenzocarbazole backbone. However, they fail to specifically disclose a compound having a structure in which a carbazole is connected to a dibenzocarbazole backbone.

DISCLOSURE OF INVENTION Technical Problem

The objective of the present disclosure is to provide an organic electroluminescent compound, which can provide an organic electroluminescent device showing long lifespan, low driving voltage, and excellence in luminous efficiency such as current efficiency and power efficiency, color purity, solubility, and thermal stability. Another objective of the present disclosure is to provide an organic electroluminescent material and an organic electroluminescent device comprising the organic electroluminescent compound.

Solution to Problems

The present inventors found that the above objectives can be achieved by an organic electroluminescent compound represented by the following formula 1.

wherein

L represents a single bond, or a substituted or unsubstituted (C6-C30)arylene;

X represents —O—, —S—, —CR₁₁R₁₂—, or —NR₁₃—;

R₁₁ and R₁₂, each independently, represent a substituted or unsubstituted (C1-C30)alkyl, a substituted or unsubstituted (C6-C30)aryl, or a substituted or unsubstituted 5- to 30-membered heteroaryl, or may be linked to an adjacent substituent(s) to form a substituted or unsubstituted, (C3-C30), mono- or polycyclic, alicyclic or aromatic ring, whose carbon atom(s) may be replaced with at least one hetero atom selected from nitrogen, oxygen, and sulfur;

R₁₃ represents a substituted or unsubstituted (C6-C30)aryl, or a substituted or unsubstituted 5- to 30-membered heteroaryl;

R₁ to R₄, each independently, represent hydrogen, deuterium, a halogen, a cyano, a substituted or unsubstituted (C1-C30)alkyl, a substituted or unsubstituted (C6-C30)aryl, a substituted or unsubstituted 5- to 30-membered heteroaryl, a substituted or unsubstituted (C3-C30)cycloalkyl, a substituted or unsubstituted (C1-C30)alkoxy, a substituted or unsubstituted tri(C1-C30)alkylsilyl, a substituted or unsubstituted di(C1-C30)alkyl(C6-C30)arylsilyl, a substituted or unsubstituted (C1-C30)alkyldi(C6-C30)arylsilyl, a substituted or unsubstituted tri(C6-C30)arylsilyl, a substituted or unsubstituted mono- or di-(C1-C30)alkylamino, a substituted or unsubstituted mono- or di-(C6-C30)arylamino, or a substituted or unsubstituted (C1-C30)alkyl(C6-C30)arylamino;

R₁ and R₄, each independently, may be linked to an adjacent substituent(s) to form a substituted or unsubstituted, (C3-C30), mono- or polycyclic, alicyclic or aromatic ring, whose carbon atom(s) may be replaced with at least one hetero atom selected from nitrogen, oxygen and sulfur;

a represents an integer of 0 to 4; where a is 2 or more, each of R₁ may be the same or different;

b and c, each independently, represent an integer of 0 to 6; where b or c is 2 or more, each of R₂ or R₃ may be the same or different;

d represents an integer of 0 to 3; where d is 2 or more, each of R₄ may be the same or different;

e represents 0 or 1; provided that where e is 0, b+c=1 or more, and at least one of R₂ and R₃ represents a substituted or unsubstituted 5- to 30-membered heteroaryl; and

the heteroaryl contains at least one hetero atom selected from B, N, O, S, Si, and P.

Advantageous Effects of Invention

The organic electroluminescent compound of the present disclosure has good color purity, solubility, and thermal stability. By comprising the organic electroluminescent compound or an organic electroluminescent material comprising the compound of the present disclosure, an organic electroluminescent device showing low driving voltage, excellent current and power efficiencies, and significantly improved lifespan can be provided.

MODE FOR THE INVENTION

Hereinafter, the present disclosure will be described in detail. However, the following description is intended to explain the invention, and is not meant in any way to restrict the scope of the invention.

The present disclosure provides the organic electroluminescent compound represented by formula 1 above, an organic electroluminescent material comprising the organic electroluminescent compound, and an organic electroluminescent device comprising the compound.

The details of the organic electroluminescent compound of formula 1 are as follows.

Herein, “alkyl” includes methyl, ethyl, n-propyl, isopropyl, n-butyl, isobutyl, tert-butyl, etc. “Cycloalkyl” includes cyclopropyl, cyclobutyl, cyclopentyl, cyclohexyl, etc. Furthermore, “aryl(ene)” indicates a monocyclic or fused ring radical derived from an aromatic hydrocarbon, and includes a spiro compound in which two rings are connected through one atom. The aryl includes phenyl, biphenyl, terphenyl, naphthyl, binaphthyl, phenylnaphthyl, naphthylphenyl, fluorenyl, phenylfluorenyl, benzofluorenyl, dibenzofluorenyl, phenanthrenyl, phenylphenanthrenyl, anthracenyl, indenyl, triphenylenyl, pyrenyl, tetracenyl, perylenyl, chrysenyl, naphthacenyl, fluoranthenyl, spirobifluorenyl, etc. “3- to 30-membered heteroaryl(ene)” indicates an aryl group having 3 to 30 ring backbone atoms including at least one, preferably 1 to 4, hetero atom selected from the group consisting of B, N, O, S, Si, and P, preferably O, S, and N; may be a monocyclic ring, or a fused ring condensed with at least one benzene ring; may be partially saturated; may be one formed by linking at least one heteroaryl or aryl group to a heteroaryl group via a single bond(s); and includes a monocyclic ring-type heteroaryl such as furyl, thiophenyl, pyrrolyl, imidazolyl, pyrazolyl, thiazolyl, thiadiazolyl, isothiazolyl, isoxazolyl, oxazolyl, oxadiazolyl, triazinyl, tetrazinyl, triazolyl, tetrazolyl, furazanyl, pyridyl, pyrazinyl, pyrimidyl, pyridazinyl, etc., and a fused ring-type heteroaryl such as benzofuranyl, benzothiophenyl, isobenzofuranyl, dibenzofuranyl, dibenzothiophenyl, benzoimidazolyl, benzothiazolyl, benzoisothiazolyl, benzoisoxazolyl, benzoxazolyl, isoindolyl, indolyl, indazolyl, benzothiadiazolyl, quinolyl, isoquinolyl, cinnolinyl, quinazolinyl, quinoxalinyl, carbazolyl, phenoxazinyl, phenanthridinyl, benzodioxolyl, dihydroacridinyl, etc. Furthermore, “halogen” includes F, Cl, Br, and I.

Herein, “substituted” in the expression, “substituted or unsubstituted,” means that a hydrogen atom in a certain functional group is replaced with another atom or group, i.e. a substituent. In the present disclosure, the substituents for the substituted alkyl, the substituted aryl, the substituted heteroaryl, the substituted cycloalkyl, the substituted alkoxy, the substituted trialkylsilyl, the substituted dialkylarylsilyl, the substituted alkyldiarylsilyl, the substituted triarylsilyl, the substituted mono- or di-alkylamino, the substituted mono- or di-arylamino, and the substituted alkylarylamino in L, R₁ to R₄, and R₁₁ to R₁₃, each independently, may be at least one selected from the group consisting of deuterium, a halogen, a cyano, a carboxy, a nitro, a hydroxy, a (C1-C30)alkyl, a halo(C1-C30)alkyl, a (C2-C30)alkenyl, a (C2-C30)alkynyl, a (C1-C30)alkoxy, a (C1-C30)alkylthio, a (C3-C30)cycloalkyl, a (C3-C30)cycloalkenyl, a 3- to 7-membered heterocycloalkyl, a (C6-C30)aryloxy, a (C6-C30)arylthio, a 5- to 30-membered heteroaryl unsubstituted or substituted with a (C6-C30)aryl, a (C6-C30)aryl unsubstituted or substituted with a 5- to 30-membered heteroaryl, a tri(C1-C30)alkylsilyl, a tri(C6-C30)arylsilyl, a di(C1-C30)alkyl(C6-C30)arylsilyl, a (C1-C30)alkyldi(C6-C30)arylsilyl, an amino, a mono- or di-(C1-C30)alkylamino, a mono- or di-(C6-C30)arylamino, a (C1-C30)alkyl(C6-C30)arylamino, a (C1-C30)alkylcarbonyl, a (C1-C30)alkoxycarbonyl, a (C6-C30)arylcarbonyl, a di(C6-C30)arylboronyl, a di(C1-C30)alkylboronyl, a (C1-C30)alkyl(C6-C30)arylboronyl, a (C6-C30)aryl(C1-C30)alkyl, and a (C1-C30)alkyl(C6-C30)aryl; and preferably at least one selected from the group consisting of deuterium, a halogen, a (C1-C20)alkyl, a halo(C1-C20)alkyl, a 6- to 20-membered heteroaryl unsubstituted or substituted with a (C6-C20)aryl, a (C6-C20)aryl unsubstituted or substituted with a 6- to 20-membered heteroaryl, a tri(C6-C20)arylsilyl, a di(C1-C20)alkyl(C6-C20)arylsilyl, a (C1-C20)alkyldi(C6-C20)arylsilyl, a mono- or di-(C6-C20)arylamino, a (C1-C20)alkyl(C6-C20)arylamino, a (C6-C20)aryl(C1-C20)alkyl, and a (C1-C20)alkyl(C6-C20)aryl.

Preferably, L may represent a single bond or a substituted or unsubstituted (C6-C20)arylene. Specifically, L may represent a single bond, a substituted or unsubstituted phenylene, a substituted or unsubstituted naphthylene, a substituted or unsubstituted biphenylene, a substituted or unsubstituted anthracenylene, a substituted or unsubstituted phenanthrenylene, a substituted or unsubstituted terphenylene, a substituted or unsubstituted tetracenylene, a substituted or unsubstituted chrysenylene, a substituted or unsubstituted pyrenylene, a substituted or unsubstituted triphenylenylene, or a substituted or unsubstituted fluoranthenylene. For the substituted arylene of L, the substituent may be preferably, a (C1-C20)alkyl, a (C6-C20)aryl unsubstituted or substituted with a 6- to 20-membered heteroaryl, or a 6- to 20-membered heteroaryl unsubstituted or substituted with a (C6-C20)aryl; and more preferably, a (C1-C6)alkyl, phenyl, naphthyl, biphenyl, carbazolyl unsubstituted or substituted with phenyl, or phenyl substituted with carbazolyl unsubstituted or substituted with phenyl.

X represents —O—, —S—, —CR₁₁R₁₂—, or —NR₁₃—. X may represent specifically, —O—, —S—, or —NR₁₃—, and more specifically —NR₁₃—.

Preferably, R₁₁ and R₁₂, each independently, may represent a substituted or unsubstituted (C1-C20)alkyl, or a substituted or unsubstituted (C6-C20)aryl, or may be linked to each other to form a substituted or unsubstituted (C3-C20), mono- or polycyclic aromatic ring. Specifically, R₁₁ and R₁₂, each independently, may represent a substituted or unsubstituted (C1-C10)alkyl, a substituted or unsubstituted phenyl, a substituted or unsubstituted biphenyl, or a substituted or unsubstituted naphthyl, or may be linked to each other to form spirobifluorenyl along with the ring containing X. Preferably, R₁₁ and R₁₂ may be unsubstituted groups.

Preferably, R₁₃ may represent a substituted or unsubstituted (C6-C20)aryl. Specifically, R₁₃ may represent a substituted or unsubstituted phenyl, a substituted or unsubstituted naphthyl, a substituted or unsubstituted biphenyl, a substituted or unsubstituted phenyl-naphthyl, a substituted or unsubstituted naphthyl-phenyl, a substituted or unsubstituted anthracenyl, a substituted or unsubstituted phenanthrenyl, a substituted or unsubstituted terphenyl, a substituted or unsubstituted tetracenyl, a substituted or unsubstituted chrysenyl, a substituted or unsubstituted pyrenyl, a substituted or unsubstituted triphenylenyl, or a substituted or unsubstituted fluoranthenyl. Preferably, R₁₃ may be an unsubstituted group.

Preferably, R₁ and R₄, each independently, may represent hydrogen, a substituted or unsubstituted (C1-C20)alkyl, a substituted or unsubstituted (C6-C20)aryl, or a substituted or unsubstituted 5- to 20-membered heteroaryl, or may be linked to an adjacent substituent(s) to form a substituted or unsubstituted (C3-C20), mono- or polycyclic aromatic ring. Specifically, R₁ and R₄, each independently, may represent hydrogen, a substituted or unsubstituted phenyl, a substituted or unsubstituted biphenyl, or a substituted or unsubstituted naphthyl, or may be linked to an adjacent substituent(s) to form a substituted or unsubstituted benzene ring or a substituted or unsubstituted naphthalene ring. Preferably, R₁ and R₄ may be unsubstituted groups.

Preferably, R₂ and R₃, each independently, may represent hydrogen, a substituted or unsubstituted (C1-C20)alkyl, a substituted or unsubstituted (C6-C20)aryl, or a substituted or unsubstituted 5- to 20-membered heteroaryl, provided that where e is 0, b+c=1 or more, and at least one of R₂ and R₃ may represent a substituted or unsubstituted 13- to 25-membered heteroaryl. Specifically, R₂ and R₃, each independently, may represent hydrogen, a substituted or unsubstituted phenyl, a substituted or unsubstituted naphthyl, a substituted or unsubstituted biphenyl, a substituted or unsubstituted dibenzofuranyl, a substituted or unsubstituted dibenzothiophenyl, a substituted or unsubstituted carbazolyl, a substituted or unsubstituted benzocarbazolyl, or a substituted or unsubstituted dibenzocarbazolyl, provided that where e is 0, b+c=1 or more, and at least one of R₂ and R₃ may represent a substituted or unsubstituted dibenzofuranyl, a substituted or unsubstituted dibenzothiophenyl, a substituted or unsubstituted carbazolyl, a substituted or unsubstituted benzocarbazolyl, or a substituted or unsubstituted dibenzocarbazolyl. Specifically, R₂ and R₃, each independently, may be selected from hydrogen and the following formulae 2-1 to 2-3. In particular, where e is 0, b+c=1 or more, and at least one of R₂ and R₃ may be preferably selected from the following formulae 2-1 to 2-3.

wherein

L_(a), L_(b), and L, each independently, represent a single bond, or a substituted or unsubstituted (C6-C30)arylene;

Z represents —S—, —O—, —NR₂₃—, or —CR₂₄R₂₅—;

R₂₀, and R₂₃ to R₂₅, each independently, represent a substituted or unsubstituted (C1-C30)alkyl, a substituted or unsubstituted (C6-C30)aryl, or a substituted or unsubstituted 3- to 30-membered heteroaryl, or may be linked to an adjacent substituent(s) to form a substituted or unsubstituted (C3-C30), mono- or polycyclic, alicyclic or aromatic ring, whose carbon atom(s) may be replaced with at least one hetero atom selected from nitrogen, oxygen, and sulfur;

R₁₄ to R₁₉, each independently, represent hydrogen, deuterium, a halogen, a cyano, a substituted or unsubstituted (C1-C30)alkyl, a substituted or unsubstituted (C3-C30)cycloalkyl, a substituted or unsubstituted (C6-C30)aryl, a substituted or unsubstituted 3- to 30-membered heteroaryl, a substituted or unsubstituted tri(C1-C30)alkylsilyl, a substituted or unsubstituted tri(C6-C30)arylsilyl, a substituted or unsubstituted di(C1-C30)alkyl(C6-C30)arylsilyl, a substituted or unsubstituted (C1-C30)alkyldi(C6-C30)arylsilyl, a substituted or unsubstituted mono- or di-(C1-C30)alkylamino, a substituted or unsubstituted mono- or di-(C6-C30)arylamino, or a substituted or unsubstituted (C1-C30)alkyl(C6-C30)arylamino, or may be linked to an adjacent substituent(s) to form a substituted or unsubstituted (C3-C30), mono- or polycyclic, alicyclic or aromatic ring, whose carbon atom(s) may be replaced with at least one hetero atom selected from nitrogen, oxygen, and sulfur;

f represents an integer of 0 to 3; g, h, i, and k, each independently, represent an integer of 0 to 4; j represents an integer of 0 to 5; where f, g, h, i, j, or k is 2 or more, each of R₁₄, R₁₅, R₁₆, R₁₇, R₁₈, or R₁₉ may be the same or different;

the heteroaryl contains at least one hetero atom selected from N, O, and S; and

* represents a bonding site.

Specifically, L_(a) to L_(c), each independently, may represent a single bond, or a substituted or unsubstituted (C6-C18)arylene. More specifically, L_(a) to L_(c), each independently, may represent a single bond, a substituted or unsubstituted phenylene, a substituted or unsubstituted biphenylene, or a substituted or unsubstituted naphthylene.

Specifically, Z may represent —NR₂₃—.

Specifically, R₂₀ and R₂₃ to R₂₅, each independently, may represent a substituted or unsubstituted (C1-C10)alkyl, or a substituted or unsubstituted (C6-C18)aryl, or may be linked to an adjacent substituent(s) to form a substituted or unsubstituted (C3-C30), mono- or polycyclic aromatic ring. More specifically, R₂₀ and R₂₃ to R₂₅, each independently, may represent a substituted or unsubstituted (C1-C6)alkyl, a substituted or unsubstituted phenyl, a substituted or unsubstituted biphenyl, or a substituted or unsubstituted naphthyl.

Specifically, R₁₄ to R₁₉, each independently, may represent hydrogen, a substituted or unsubstituted (C1-C10)alkyl, or a substituted or unsubstituted (C6-C18)aryl, or may be linked to an adjacent substituent(s) to form a substituted or unsubstituted (C3-C30) mono- or polycyclic aromatic ring, whose carbon atom(s) may be replaced with one to three hetero atom(s) selected from nitrogen, oxygen, and sulfur. More specifically, R₁₄ to R₁₉, each independently, may represent hydrogen, a substituted or unsubstituted phenyl, a substituted or unsubstituted biphenyl, or a substituted or unsubstituted naphthyl, or may be linked to an adjacent substituent(s) to form a benzene ring or a naphthalene ring.

According to another embodiment of the present disclosure, L may represent a single bond, or a substituted or unsubstituted (C6-C20)arylene; X may represent —O—, —S—, —CR₁₁R₁₂—, or —NR₁₃—; R₁₁ and R₁₂, each independently, may represent a substituted or unsubstituted (C1-C20)alkyl, or a substituted or unsubstituted (C6-C20)aryl, or may be linked to each other to form a substituted or unsubstituted (C3-C20), mono- or polycyclic aromatic ring; R₁₃ may represent a substituted or unsubstituted (C6-C20)aryl; R₁ and R₄, each independently, may represent hydrogen, a substituted or unsubstituted (C1-C20)alkyl, a substituted or unsubstituted (C6-C20)aryl, or a substituted or unsubstituted 5- to 20-membered heteroaryl, or may be linked to an adjacent substituent(s) to form a substituted or unsubstituted, (C3-C20), mono- or polycyclic aromatic ring; R₂ and R₃, each independently, may represent hydrogen, a substituted or unsubstituted (C1-C20)alkyl, a substituted or unsubstituted (C6-C20)aryl, or a substituted or unsubstituted 5- to 20-membered heteroaryl; provided that where e is 0, b+c=1 or more, and at least one of R₂ and R₃ may represent a substituted or unsubstituted 13- to 25-membered heteroaryl; and the heteroaryl may contain at least one hetero atom selected from N, O, and S.

According to another embodiment of the present disclosure, e may represent 1; X may represent —O—, —S—, or —NR₁₃—; R₁₃ may represent a substituted or unsubstituted phenyl, a substituted or unsubstituted naphthyl, a substituted or unsubstituted biphenyl, a substituted or unsubstituted phenyl-naphthyl, a substituted or unsubstituted naphthyl-phenyl, a substituted or unsubstituted anthracenyl, a substituted or unsubstituted phenanthrenyl, a substituted or unsubstituted terphenyl, a substituted or unsubstituted tetracenyl, a substituted or unsubstituted chrysenyl, a substituted or unsubstituted pyrenyl, a substituted or unsubstituted triphenylenyl, or a substituted or unsubstituted fluoranthenyl; and R₁ and R₄, each independently, may represent hydrogen, a substituted or unsubstituted phenyl, a substituted or unsubstituted biphenyl, or a substituted or unsubstituted naphthyl, or may be linked to an adjacent substituent(s) to form a substituted or unsubstituted benzene or naphthalene ring.

According to another embodiment of the present disclosure, e may represent 0; L may represent a substituted or unsubstituted (C6-C20)arylene; b+c=1 or more; and at least one of R₂ and R₃ may be selected from formulae 2-1 to 2-3.

More specifically, the organic electroluminescent compound of formula 1 includes the following, but is not limited thereto:

The organic electroluminescent compound of the present disclosure can be prepared by a synthetic method known to one skilled in the art. For example, it can be prepared according to any of the following reaction scheme 1 or 2.

wherein X, R₁ to R₄, L, a, b, c, d, and e are as defined in formula 1 above, and Hal represents a halogen.

According to another embodiment of the present disclosure, an organic electroluminescent material comprising the organic electroluminescent compound of formula 1, and an organic electroluminescent device comprising the material are provided.

The material may consist of the organic electroluminescent compound of the present disclosure. Otherwise, the material may further comprise a conventional compound(s) which has been comprised for an organic electroluminescent material.

Herein, the organic electroluminescent material indicates a material which is used for an organic electroluminescence.

The organic electroluminescent material may be a material for an organic electroluminescent device, which is used for preparing an organic electroluminescent device.

The organic electroluminescent material may be preferably, a material to be used for a light-emitting layer of an organic electroluminescent device, more preferably, a host material to be combined with a dopant material in a light-emitting layer of an organic electroluminescent device, and even more preferably a phosphorescent host material. The host material may further comprise a compound represented by the following formula 3. When the host material further comprises the compound of formula 3, the weight ratio between the compound of formula 1 and the compound of formula 3 may be in the range of 1:99 to 99:1, and specifically 30:70 to 70:30.

Preferably, the organic electroluminescent material may be a hole transport material. More preferably, the organic electroluminescent material may be a material to be used for a hole transport layer of an organic electroluminescent device.

The organic electroluminescent device of the present disclosure may comprise a first electrode, a second electrode, and at least one organic layer disposed between the first and second electrodes. The organic layer may comprise at least one organic electroluminescent compound of formula 1.

One of the first and second electrodes may be an anode, and the other may be a cathode. The organic layer may comprise a light-emitting layer, and may further comprise at least one layer selected from a hole injection layer, a hole transport layer, an electron transport layer, an electron injection layer, an interlayer, a hole blocking layer, an electron buffering layer, and an electron blocking layer.

The organic electroluminescent compound of formula 1 of the present disclosure may be comprised in the light-emitting layer. When used in the light-emitting layer, the organic electroluminescent compound of formula 1 of the present disclosure may be comprised as a host material, preferably a phosphorescent host material, and more preferably a phosphorescent red light-emitting host material. Preferably, the light-emitting layer may further comprise at least one or more dopants, and, if necessary, a second host material other than the compound of formula 1 of the present disclosure. The weight ratio between the first host material and the second host material is in the range of 1:99 to 99:1 and specifically 30:70 to 70:30.

The second host material may be from any of the known phosphorescent hosts. The compound selected from the group consisting of compounds of formula 3 is preferably the second host material in view of luminous efficiency.

According to another embodiment of the present disclosure, an organic electroluminescent device comprising an anode, a cathode, and an organic layer between the anode and the cathode, wherein the organic layer comprises one or more light-emitting layers; at least one of the one or more light-emitting layers comprises one or more dopant compounds and two or more host compounds; a first host compound of the host compounds is represented by formula 1; and a second host compound is represented by formula 3 is provided.

wherein

Ma represents a substituted or unsubstituted nitrogen-containing 5- to 11-membered heteroaryl;

La represents a single bond, or a substituted or unsubstituted (C6-C30)arylene;

Xa to Xh, each independently, represent hydrogen, deuterium, a halogen, a cyano, a substituted or unsubstituted (C1-C30)alkyl, a substituted or unsubstituted (C2-C30)alkenyl, a substituted or unsubstituted (C2-C30)alkynyl, a substituted or unsubstituted (C3-C30)cycloalkyl, a substituted or unsubstituted (C6-C60)aryl, a substituted or unsubstituted 3- to 30-membered heteroaryl, a substituted or unsubstituted tri(C1-C30)alkylsilyl, a substituted or unsubstituted tri(C6-C30)arylsilyl, a substituted or unsubstituted di(C1-C30)alkyl(C6-C30)arylsilyl, a substituted or unsubstituted (C1-C30)alkyldi(C6-C30)arylsilyl, or a substituted or unsubstituted mono- or di-(C6-C30)arylamino; or may be linked to an adjacent substituent(s) to form a substituted or unsubstituted (C3-C30), mono- or polycyclic, alicyclic or aromatic ring, whose carbon atom(s) may be replaced with at least one hetero atom selected from nitrogen, oxygen, and sulfur; and

the heteroaryl contains at least one hetero atom selected from B, N, O, S, Si, and P.

In formula 3, specifically, Ma may represent a substituted or unsubstituted pyrrolyl, a substituted or unsubstituted imidazolyl, a substituted or unsubstituted pyrazolyl, a substituted or unsubstituted triazinyl, a substituted or unsubstituted tetrazinyl, a substituted or unsubstituted triazolyl, a substituted or unsubstituted tetrazolyl, a substituted or unsubstituted pyridyl, a substituted or unsubstituted pyrazinyl, a substituted or unsubstituted pyrimidinyl, a substituted or unsubstituted pyridazinyl, a substituted or unsubstituted benzimidazolyl, a substituted or unsubstituted isoindolyl, a substituted or unsubstituted indolyl, a substituted or unsubstituted indazolyl, a substituted or unsubstituted quinolyl, a substituted or unsubstituted isoquinolyl, a substituted or unsubstituted cinnolinyl, a substituted or unsubstituted quinazolinyl, a substituted or unsubstituted naphthyridinyl, or a substituted or unsubstituted quinoxalinyl. More specifically, Ma may represent a substituted or unsubstituted triazinyl, a substituted or unsubstituted pyrimidinyl, a substituted or unsubstituted pyridyl, a substituted or unsubstituted quinolyl, a substituted or unsubstituted isoquinolyl, a substituted or unsubstituted quinazolinyl, a substituted or unsubstituted naphthyridinyl, or a substituted or unsubstituted quinoxalinyl. Specifically, the substituents for the substituted nitrogen-containing 5- to 11-membered heteroaryl of Ma may be a (C6-C18)aryl unsubstituted or substituted with a cyano, a halogen, a (C1-C10)alkyl, or a tri(C6-C12)arylsilyl.

In formula 3, specifically, La may represent a single bond, a substituted or unsubstituted phenylene, a substituted or unsubstituted naphthylene, or a substituted or unsubstituted biphenylene.

In formula 3, specifically, Xa to Xh, each independently, may represent hydrogen, a cyano, a substituted or unsubstituted (C6-C15)aryl, a substituted or unsubstituted 6- to 20-membered heteroaryl, or a substituted or unsubstituted tri(C6-C15)arylsilyl, or may be linked to an adjacent substituent(s) to form a substituted or unsubstituted 6- to 20-membered, mono- or polycyclic, aromatic ring, whose carbon atom(s) may be replaced with at least one hetero atom selected from nitrogen, oxygen, and sulfur. Specifically, the formed mono- or polycyclic aromatic ring may be a substituted or unsubstituted benzene, a substituted or unsubstituted indole, a substituted or unsubstituted benzindole, a substituted or unsubstituted indene, a substituted or unsubstituted benzofuran, or a substituted or unsubstituted benzothiophene.

Specifically, the second host material includes the following, but is not limited thereto:

The dopant to be comprised in the organic electroluminescent device of the present disclosure is preferably at least one phosphorescent dopant. The phosphorescent dopant material for the organic electroluminescent device of the present disclosure is not limited, but may be preferably selected from metallated complex compounds of iridium (Ir), osmium (Os), copper (Cu) or platinum (Pt), more preferably selected from ortho-metallated complex compounds of iridium (Ir), osmium (Os), copper (Cu) or platinum (Pt), and even more preferably ortho-metallated iridium complex compounds.

Preferably, the dopant to be comprised in the organic electroluminescent device of the present disclosure may be selected from the group consisting of compounds represented by the following formulae 101 to 103.

wherein L is selected from the following structures:

R₁₀₀ represents hydrogen, a substituted or unsubstituted (C1-C30)alkyl, or a substituted or unsubstituted (C3-C30)cycloalkyl; R₁₀₁ to R₁₀₉ and R₁₁₁ to R₁₂₃, each independently, represent hydrogen, deuterium, a halogen, a (C1-C30)alkyl unsubstituted or substituted with a halogen, a substituted or unsubstituted (C3-C30)cycloalkyl, a substituted or unsubstituted (C6-C30)aryl, a cyano, or a substituted or unsubstituted (C1-C30)alkoxy; R₁₀₆ to R₁₀₉ may be linked to an adjacent substituent(s) to form a substituted or unsubstituted fused ring, for example, fluorene unsubstituted or substituted with alkyl, dibenzothiophene unsubstituted or substituted with alkyl, or dibenzofuran unsubstituted or substituted with alkyl; R₁₂₀ to R₁₂₃ may be linked to an adjacent substituent(s) to form a substituted or unsubstituted fused ring, for example, quinoline unsubstituted or substituted with alkyl or aryl; R₁₂₄ to R₁₂₇, each independently, represent hydrogen, deuterium, a halogen, a substituted or unsubstituted (C1-C30)alkyl, or a substituted or unsubstituted (C6-C30)aryl; R₁₂₄ to R₁₂₇ may be linked to an adjacent substituent(s) to form a substituted or unsubstituted fused ring, for example, fluorene unsubstituted or substituted with alkyl, dibenzothiophene unsubstituted or substituted with alkyl, or dibenzofuran unsubstituted or substituted with alkyl; R₂₀₁ to R₂₁₁, each independently, represent hydrogen, deuterium, a halogen, a (C1-C30)alkyl unsubstituted or substituted with a halogen, a substituted or unsubstituted (C3-C30)cycloalkyl, or a substituted or unsubstituted (C6-C30)aryl; R₂₀₈ to R₂₁₁ may be linked to an adjacent substituent(s) to form a substituted or unsubstituted fused ring, for example, fluorene unsubstituted or substituted with alkyl, dibenzothiophene unsubstituted or substituted with alkyl, or dibenzofuran unsubstituted or substituted with alkyl; r, s, and t, each independently, represent an integer of 1 to 3; where r or s is an integer of 2 or more, each of R₁₀₀ may be the same or different.

Specifically, the dopant material includes the following, but is not limited thereto.

According to an additional aspect of the present disclosure, a mixture or composition for preparing an organic electroluminescent device is provided. The mixture or composition comprises the compound of the present disclosure. The mixture or composition may be used for preparing a light-emitting layer or a hole transport layer of an organic electroluminescent device. The mixture or composition for preparing a light-emitting layer of an organic electroluminescent device may be a mixture or composition for preparing a phosphorescent or fluorescent light-emitting layer, and specifically a phosphorescent red light-emitting layer of an organic electroluminescent device. Where the compound of the present disclosure is comprised in the mixture or composition for preparing a hole transport layer of an organic electroluminescent device, it may be comprised as a hole transport material. Where the compound of the present disclosure is comprised in the mixture or composition for preparing a light-emitting layer of an organic electroluminescent device, it may be comprised as a host material. Where the compound of the present disclosure is comprised as a host material, the mixture or composition may further comprise a second host material. The weight ratio between the first host material and the second host material is in the range of 1:99 to 99:1, and specifically 30:70 to 70:30.

The organic electroluminescent device of the present disclosure may comprise a first electrode, a second electrode, and at least one organic layer disposed between the first and second electrodes, wherein the organic layer may comprise a light-emitting layer or a hole transport layer, and the light-emitting layer or the hole transport layer may comprise the mixture or composition for an organic electroluminescent device of the present disclosure.

The organic electroluminescent device of the present disclosure may further comprise, in addition to the organic electroluminescent compound of formula 1, at least one compound selected from the group consisting of arylamine-based compounds and styrylarylamine-based compounds.

In the organic electroluminescent device of the present disclosure, the organic layer may further comprise, in addition to the compound of formula 1, at least one metal selected from the group consisting of metals of Group 1, metals of Group 2, transition metals of the 4^(th) period, transition metals of the 5^(th) period, lanthanides and organic metals of the d-transition elements of the Periodic Table, or at least one complex compound comprising the metal. The organic layer may further comprise a light-emitting layer and a charge generating layer.

In addition, the organic electroluminescent device of the present disclosure may emit white light by further comprising at least one light-emitting layer, which comprises a blue electroluminescent compound, a red electroluminescent compound or a green electroluminescent compound known in the art, besides the compound of the present disclosure. If necessary, the organic electroluminescent device of the present disclosure may further comprise a yellow- or orange-light-emitting layer.

In the organic electroluminescent device of the present disclosure, preferably, at least one layer (hereinafter, “a surface layer”) may be placed on an inner surface(s) of one or both electrode(s), selected from a chalcogenide layer, a metal halide layer and a metal oxide layer. Specifically, a chalcogenide (includes oxides) layer of silicon or aluminum is preferably placed on an anode surface of an electroluminescent medium layer, and a metal halide layer or a metal oxide layer is preferably placed on a cathode surface of an electroluminescent medium layer. Such a surface layer provides operation stability for the organic electroluminescent device. Preferably, the chalcogenide includes SiO_(X)(1≦X≦2), AlO_(X)(1≦X≦1.5), SiON, SiAlON, etc.; the metal halide includes LiF, MgF₂, CaF₂, a rare earth metal fluoride, etc.; and the metal oxide includes Cs₂O, Li₂O, MgO, SrO, BaO, CaO, etc.

In the organic electroluminescent device of the present disclosure, a mixed region of an electron transport compound and a reductive dopant, or a mixed region of a hole transport compound and an oxidative dopant may be placed on at least one surface of a pair of electrodes. In this case, the electron transport compound is reduced to an anion, and thus it becomes easier to inject and transport electrons from the mixed region to an electroluminescent medium. Furthermore, the hole transport compound is oxidized to a cation, and thus it becomes easier to inject and transport holes from the mixed region to the electroluminescent medium. Preferably, the oxidative dopant includes various Lewis acids and acceptor compounds, and the reductive dopant includes alkali metals, alkali metal compounds, alkaline earth metals, rare-earth metals, and mixtures thereof. A reductive dopant layer may be employed as a charge generating layer to prepare an electroluminescent device having two or more light-emitting layers and emitting white light.

In order to form each layer of the organic electroluminescent device of the present disclosure, dry film-forming methods such as vacuum evaporation, sputtering, plasma and ion plating methods, or wet film-forming methods such as ink jet printing, nozzle printing, slot coating, spin coating, dip coating, and flow coating methods can be used.

When using a wet film-forming method, a thin film can be formed by dissolving or diffusing materials forming each layer into any suitable solvent such as ethanol, chloroform, tetrahydrofuran, dioxane, etc. The solvent can be any solvent where the materials forming each layer can be dissolved or diffused, and where there are no problems in film-formation capability.

In the organic electroluminescent device of the present disclosure, two or more host compounds for a light-emitting layer may be co-evaporated or mixture-evaporated. Herein, a co-evaporation indicates a process for two or more materials to be deposited as a mixture, by introducing each of the two or more materials into respective crucible cells, and applying electric current to the cells for each of the materials to be evaporated. Herein, a mixture-evaporation indicates a process for two or more materials to be deposited as a mixture, by mixing the two or more materials in one crucible cell before the deposition, and applying electric current to the cell for the mixture to be evaporated.

A display system or a lighting system using the organic electroluminescent device of the present disclosure can be produced.

Hereinafter, the organic electroluminescent compound of the present disclosure, the preparation method of the compound, and the luminescent properties of the device will be explained in detail with reference to the following examples.

EXAMPLE 1: PREPARATION OF COMPOUND H-1

Preparation of Compound 1-1

After dissolving 7H-dibenzo[c,g]carbazole (10 g, 37.40 mmol), 1-bromo-4-iodobenzene (21 g, 74.80 mmol), CuI (3.6 g, 18.70 mmol), ethylenediamine (EDA) (5 mL, 74.80 mmol), and K₃PO₄ (20 g, 93.50 mmol) in toluene (200 mL) of a flask, the mixture was under reflux at 120° C. for 2 hours. After completion of the reaction, the mixture was filtered under reduced pressure with methylene chloride (MC), and subjected to column chromatography. Methanol was added to the resultant. The obtained solid was filtered under reduced pressure to obtain compound 1-1 (12.2 g, yield: 77%).

Preparation of Compound H-1

After dissolving compound 1-1 (8 g, 18.90 mmol), (9-phenyl-9H-carbazol-3-yl)boronic acid (6.6 g, 22.70 mmol), Pd(PPh₃)₄ (2.2 g, 1.89 mmol), and K₂CO₃ (7.8 g, 56.70 mmol) in toluene (100 mL), ethanol (50 mL), and H₂O (50 mL), the mixture was under reflux at 120° C. for 4 hours. After completion of the reaction, the mixture was extracted with ethyl acetate (EA), dried with MgSO₄, and subjected to column chromatography. Methanol was added to the resultant. The obtained solid was filtered under reduced pressure, recrystallized with toluene, and filtered under reduced pressure to obtain compound H-1 (5.3 g, yield: 48%).

Molecular Weight UV PL Melting Point (M.P.) 584.71 382 nm 397 nm 264.8° C.

EXAMPLE 2: PREPARATION OF COMPOUND H-55

Preparation of Compound 2-1

After dissolving 7H-dibenzo[c,g]carbazole (50 g, 187 mmol) and N-bromosuccinimide (NBS) (31.6 g, 177 mmol) in dimethylformamide (DMF) (1 L) of a flask, the mixture was stirred at room temperature for 5 hours. After completion of the reaction, the mixture was extracted with EA, dried with MgSO₄, and subjected to column chromatography. Hexane was added to the resultant. The obtained solid was filtered under reduced pressure to obtain compound 2-1 (52 g, yield: 80%).

Preparation of Compound 2-2

After dissolving compound 2-1 (52 g, 150.2 mmol), (9-phenyl-9H-carbazol-3-yl)boronic acid (46.1 g, 150.2 mmol), Pd(PPh₃)₄ (8.7 g, 1.6 mmol), and K₂CO₃ (51.9 g, 375.5 mmol) in toluene (570 mL), ethanol (100 mL), and distilled water (190 mL), the mixture was under reflux at 120° C. for 4 hours. After completion of the reaction, the mixture was extracted with MC, dried with MgSO₄, and subjected to column chromatography. Hexane was added to the resultant. The obtained solid was filtered under reduced pressure to obtain compound 2-2 (62 g, yield: 71%).

Preparation of Compound H-55

After dissolving compound 2-2 (10.0 g, 19.66 mmol), iodobenzene (4.4 mL, 39.32 mmol), CuI (1.87 g, 9.83 mmol), EDA (1.32 mL, 19.66 mmol), and Cs₂CO₃ (16.0 g, 49.15 mmol) in toluene (100 mL), the mixture was under reflux at 130° C. for 5 hours. After completion of the reaction, the mixture was filtered under reduced pressure with MC, and subjected to column chromatography. Methanol was added to the resultant. The obtained solid was filtered under reduced pressure to obtain compound H-55 (7.6 g, yield: 66%).

Molecular Weight UV PL M.P. 584.71 352 nm 423 nm 150° C.

EXAMPLE 3: PREPARATION OF COMPOUND H-56

After dissolving compound 2-2 (10.0 g, 19.66 mmol), 2-bromonaphthalene (6.9 g, 33.4 mmol), CuI (1.87 g, 9.83 mmol), EDA (1.32 mL, 19.66 mmol), and Cs₂CO₃ (16.0 g, 49.15 mmol) in toluene (100 mL), the mixture was under reflux at 130° C. for 5 hours. After completion of the reaction, the mixture was filtered under reduced pressure with MC, and subjected to column chromatography. Methanol was added to the resultant. The obtained solid was filtered under reduced pressure to obtain compound H-56 (7.6 g, yield: 61%).

Molecular Weight UV PL M.P. 634.77 334 nm 421 nm 140° C.

EXAMPLE 4: PREPARATION OF COMPOUND H-66

Preparation of Compound 4-1

After introducing 2-bromo-4-fluoro-1-nitrobenzene (50 g, 227.3 mmol), phenyl boronic acid (30.5 g, 250 mmol), Pd(PPh₃)₄ (13.1 g, 11.37 mmol), K₂CO₃ (62.8 g, 454.6 mmol), toluene (600 mL), ethanol (200 mL), and distilled water (200 mL) into a flask, the mixture was stirred under reflux for 6 hours. After cooling to room temperature, the mixture was extracted with EA and distilled water. The obtained organic layer was distilled under reduced pressure. The residue was subjected to column chromatography to obtain compound 4-1 (49 g, yield: 99%).

Preparation of Compound 4-2

After introducing 7H-dibenzo[c,g]carbazole (34.5 g, 128.9 mmol), compound 4-1 (28 g, 128.9 mmol), NaH (6.7 g, 167.6 mmol), and DMF (600 mL) into a flask, the mixture was stirred at 75° C. for 2 hours. After cooling to room temperature, MeOH (1 L) and purified water were added to the mixture. The obtained solid was filtered, and dried under reduced pressure to obtain compound 4-2 (52 g, yield: 86.8%).

Preparation of Compound 4-3

After introducing compound 4-2 (52 g, 111.9 mmol), PPh₃ (88 g, 335.8 mmol), and 1,2-dichlorobenzene (500 mL) into a flask, the mixture was stirred under reflux for 6 hours. The mixture was distilled to remove 1,2-dichlorobenzene (1,2-DCB). The residue was subjected to column chromatography to obtain compound 4-3 (39 g, yield: 75.9%).

Preparation of Compound H-66

After introducing compound 4-3 (7 g, 16.18 mmol), 2-bromonaphthalene (5.0 g, 24.27 mmol), Pd(OAc)₂ (365 mg, 1.6 mmol), P(t-Bu)₃ (1.6 mL, 3.2 mmol), NaOt-Bu (4.7 g, 48.54 mmol), and toluene (100 mL) into a flask, the mixture was stirred under reflux for 3 hours, cooled to room temperature, and extracted with ethyl acetate and purified water. The obtained organic layer was concentrated, and subjected to column chromatography to obtain compound H-66 (3.0 g, yield: 33.2%).

Molecular Weight UV PL M.P. 558.67 378 nm 397 nm 250° C.

EXAMPLE 5: PREPARATION OF COMPOUND H-25

Preparation of Compound 5-1 After introducing 7H-dibenzo[c,g]carbazole (CAS: 194-59-2, 30 g, 112.2 mmol), 4-bromoiodobenzene (63 g, 224.4 mmol), copper(I) iodide (11 g, 56.1 mmol), ethylene diamine (13 mL, 224 mmol), potassium phosphate (48 g, 224.4 mmol), and toluene (600 mL) into a reaction vessel, the mixture was stirred at 140° C. for 3 hours. After completion of the reaction, the mixture was extracted with ethyl acetate, dried with magnesium sulfate, and dried by rotary evaporator to remove a solvent. The resultant was subjected to column chromatography to obtain compound 5-1 (33.7 g, yield: 71%).

Preparation of Compound 5-3

After introducing compound 5-1 (33.7 g, 79.8 mmol), compound 5-2 (CAS: 855738-89-5, 23.4 g, 79.8 mmol), tetrakis(triphenylphosphine)palladium (2.8 g, 2.39 mmol), potassium carbonate (22 g, 100 mmol), toluene (300 mL), water (100 mL), and ethanol (100 mL) into a reaction vessel, the mixture was stirred at 140° C. for 3 hours. After completion of the reaction, the mixture was cooled to room temperature, and filtered. The obtained solid was subjected to column chromatography to obtain compound 5-3 (28.5 g, yield: 70%).

Preparation of Compound H-25

After introducing compound 5-3 (14 g, 27.5 mmol), 2-bromonaphthalene (7.4 g. 36 mmol), tris(dibenzylideneacetone)dipalladium (1.2 g, 1.38 mmol), tri-tert-butylphosphine (50 wt % xylene, 1.1 mL, 2.75 mmol), sodium t-butoxide (5.3 g, 55 mmol), and toluene (200 mL) into a reaction vessel, the mixture was stirred at 140° C. overnight. After completion of the reaction, the mixture was added dropwise to methanol, and filtered. The obtained solid was subjected to column chromatography and recrystallized to obtain compound H-25 (2 g, yield: 11%).

Molecular Weight UV PL M.P. 634.24 308 nm 396 nm 261° C.

EXAMPLE 6: PREPARATION OF COMPOUND H-34

Preparation of Compound 6-1

After dissolving 2-bromo-4-fluoro-1-nitrobenzene (30 g, 136 mmol), phenylboronic acid (18.3 g, 150 mmol), Pd(PPh₃)₄ (6.3 g, 5.4 mmol), and Na₂CO₃ (36 g, 340 mmol) in toluene (680 mL), ethanol (170 mL), and distilled water (170 mL), the mixture was under reflux at 120° C. for 3 hours. After completion of the reaction, the mixture was extracted with MC, dried with MgSO₄, and subjected to column chromatography. Hexane was added to the resultant. The obtained solid was filtered under reduced pressure to obtain compound 6-1 (29 g, yield: 98%).

Preparation of Compound 6-2

A mixture of 7H-dibenzo[c,g]carbazole (35.7 g, 134 mmol), NaH (60% in dispersion oil) (6.9 g, 173 mmol), and DMF (900 mL) in a flask was slowly stirred at 0° C. for 30 minutes. Compound 6-1 was slowly added dropwise to the reaction mixture. The reaction mixture was stirred at room temperature overnight. After completion of the reaction, the mixture was added dropwise to water. The obtained solid was subjected to column chromatography. Hexane was added to the resultant. The obtained solid was filtered under reduced pressure to obtain compound 6-2 (41 g, yield: 66%).

Preparation of compound 6-3

A mixture of compound 6-2 (41 g, 88 mmol), P(OEt)₃ (300 mL), and 1,2-DCB (300 mL) was under reflux at 180° C. for 12 hours. The reaction mixture was distilled under reduced pressure, and subjected to column chromatography. Hexane was added to the resultant. The obtained solid was filtered under reduced pressure to obtain compound 6-3 (21 g, yield: 55%).

Preparation of Compound H-34

After dissolving compound 6-3 (7 g, 16 mmol), 4-bromo-1,1′-biphenyl (5.6 g, 24 mmol), Pd(OAc)₂ (0.182 g, 0.8 mmol), P(t-Bu)₃ (0.76 mL, 1.6 mmol), and NaOtBu (2.3 g, 24 mmol) in o-xylene (80 mL), the mixture was under reflux at 150° C. for 12 hours. After completion of the reaction, the mixture was extracted with EA, dried with MgSO₄, and subjected to column chromatography. Hexane was added to the resultant. The obtained solid was filtered under reduced pressure, recrystallized with toluene, and filtered under reduced pressure to obtain compound H-34 (3.6 g, yield: 38%).

Molecular Weight UV PL M.P. 584.71 382 nm 399 nm 263° C.

EXAMPLE 7: PREPARATION OF COMPOUND H-67

Preparation of Compound 7-1

After dissolving naphthalen-2-yl boronic acid (13.4 g, 77 mmol), 1-bromo-4-iodobenzene (20 g, 71 mmol), Pd(PPh₃)₄ (3.3 g, 21.8 mmol), and Na₂CO₃ (18.8 g, 177 mmol) in toluene (360 mL), ethanol (90 mL), and distilled water (90 mL) of a flask, the mixture was under reflux at 120° C. for 4 hours. After completion of the reaction, the mixture was extracted with MC, dried with MgSO₄, and subjected to column chromatography. Hexane was added to the resultant. The obtained solid was filtered under reduced pressure to obtain compound 7-1 (7 g, yield: 35%).

Preparation of Compound H-67

After dissolving compound 7-3 (7 g, 16 mmol), compound 7-1 (6.9 g, 24 mmol), Pd(OAc)₂ (0.182 g, 0.8 mmol), P(t-Bu)₃ (0.76 mL, 1.6 mmol), and NaOtBu (2.3 g, 24 mmol) in o-xylene (80 mL), the mixture was under reflux at 150° C. for 12 hours. After completion of the reaction, the mixture was extracted with EA, dried with MgSO₄, and subjected to column chromatography. Hexane was added to the resultant. The obtained solid was filtered under reduced pressure, recrystallized with toluene, and filtered under reduced pressure to obtain compound H-67 (3 g, yield: 29%).

Molecular Weight UV PL M.P. 634.77 376 nm 397 nm 260° C.

EXAMPLE 8: PREPARATION OF COMPOUND H-68

Preparation of Compound 1-1

After introducing 2-bromo-4-fluoro-1-nitrobenzene (30 g, 136.36 mmol), 1-naphthyl boronic acid (28 g, 163.64 mmol), tetrakis(triphenylphosphine)palladium (4.7 g, 4.09 mmol), potassium carbonate (47 g, 340.90 mmol), toluene (690 mL), and ethanol (170 mL) into a reaction vessel, distilled water (170 mL) was added thereto. The mixture was stirred at 120° C. for 4 hours. After completion of the reaction, the mixture was washed with distilled water, and extracted with ethyl acetate. The obtained organic layer was dried with magnesium sulfate, dried by rotary evaporator to remove a solvent, and subjected to column chromatography to obtain compound 8-1 (33 g, yield: 92%).

Preparation of Compound 8-2

After introducing 7H-dibenzo[c,g]carbazole (25 g, 115.10 mmol) and N,N-dimethylformamide (580 mL) into a reaction vessel, sodium hydride (6 g, 149.63 mmol) was slowly added dropwise to the mixture at 0° C. under nitrogen atmosphere. The mixture was stirred at 0° C. for 30 minutes, and compound 8-1 (32 g, 120.86 mmol) was slowly added dropwise thereto. After completion of the addition, the mixture was slowly warmed to room temperature, and additionally stirred for 4 hours. After completion of the reaction, methanol was added thereto to stop the reaction. The resultant was extracted with ethyl acetate. The obtained organic layer was dried with magnesium sulfate, dried by rotary evaporator to remove a solvent, and subjected to column chromatography to obtain compound 8-2 (35 g, yield: 59%).

Preparation of Compound 8-3

After introducing compound 8-2 (35 g, 68.02 mmol) and triethylphosphite (170 mL, 0.4M) to the reaction vessel, the mixture was stirred under reflux for 4 hours. After completion of the reaction, the mixture was distilled under reduced pressure to remove triethylphosphite, and subjected to column chromatography to obtain compound 8-3 (29 g, yield: 88%).

Preparation of Compound H-68

After introducing compound 8-3 (10 g, 20.72 mmol), 2-bromonaphthalene (6.4 g, 31.08 mmol), palladium(II) acetate (0.3 g, 1.04 mmol), tri-t-butyl phosphine (1 mL, 2.08 mmol), sodium tert-butoxide (3 g, 31.08 mmol), and o-xylene (105 mL) into a reaction vessel, the mixture was stirred under reflux for 4 hours. After completion of the reaction, the mixture was washed with distilled water, and extracted with ethyl acetate. The obtained organic layer was dried with magnesium sulfate, and then dried by rotary evaporator to remove a solvent. The resultant was subjected to column chromatography to obtain compound H-68 (2.5 g, yield: 20%).

Molecular Weight UV PL M.P. 608.73 378 nm 397 nm 274° C.

EXAMPLE 9: PREPARATION OF COMPOUND H-35

Preparation of Compound 1-1

After introducing 2-bromo-4-fluoro-1-nitrobenzene (30 g, 136.36 mmol), 1-naphthyl boronic acid (28 g, 163.64 mmol), tetrakis(triphenylphosphine)palladium (4.7 g, 4.09 mmol), potassium carbonate (47 g, 340.90 mmol), toluene (690 mL), and ethanol (170 mL) into a reaction vessel, distilled water (170 mL) was added thereto. The mixture was stirred at 120° C. for 4 hours. After completion of the reaction, the mixture was washed with distilled water, and extracted with ethyl acetate. The obtained organic layer was dried with magnesium sulfate, dried by rotary evaporator to remove a solvent, and subjected to column chromatography to obtain compound 9-1 (33 g, yield: 92%).

Preparation of Compound 9-2

After introducing 7H-dibenzo[c,g]carbazole (25 g, 115.10 mmol) and N,N-dimethylformamide (580 mL) into a reaction vessel, sodium hydride (6 g, 149.63 mmol) was slowly added dropwise to the mixture at 0° C. under nitrogen atmosphere. The mixture was stirred at 0° C. for 30 minutes, and compound 9-1 (32 g, 120.86 mmol) was slowly added dropwise thereto. After completion of the addition, the mixture was slowly warmed to room temperature, and additionally stirred for 4 hours. After completion of the reaction, methanol was added thereto to stop the reaction. The resultant was extracted with ethyl acetate. The obtained organic layer was dried with magnesium sulfate, dried by rotary evaporator to remove a solvent, and subjected to column chromatography to obtain compound 9-2 (35 g, yield: 59%).

Preparation of Compound 9-3

After introducing compound 9-2 (35 g, 68.02 mmol) and triethylphosphite (170 mL, 0.4M) into a reaction vessel, the mixture was stirred under reflux for 4 hours. After completion of the reaction, the mixture was distilled under reduced pressure to remove triethylphosphite, and subjected to column chromatography to obtain compound 9-3 (29 g, yield: 88%).

Preparation of Compound H-35

After introducing compound 9-3 (10 g, 20.72 mmol), iodobenzene (4 mL, 31.08 mmol), palladium(II) acetate (0.3 g, 1.04 mmol), tri-t-butylphosphine (1 mL, 2.08 mmol), sodium tert-butoxide (3 g, 31.08 mmol), and o-xylene (105 mL) into a reaction vessel, the mixture was stirred under reflux for 4 hours. After completion of the reaction, the mixture was washed with distilled water, and extracted with ethyl acetate. The obtained organic layer was dried with magnesium sulfate, and then dried by rotary evaporator to remove a solvent. The resultant was subjected to column chromatography to obtain compound H-35 (2.8 g, yield: 24%).

Molecular Weight UV PL M.P. 558.67 378 nm 397 nm 292° C.

[Device Example 1] OLED Using the Compound of the Present Disclosure

OLED was produced using the organic electroluminescent compound of the present disclosure as follows. A transparent electrode indium tin oxide (ITO) thin film (10 Ω/sq) on a glass substrate for an OLED (Geomatec) was subjected to an ultrasonic washing with acetone, ethanol, and distilled water sequentially, and was then stored in isopropanol. The ITO substrate was then mounted on a substrate holder of a vacuum vapor depositing apparatus. HI-1 was introduced into a cell of said vacuum vapor depositing apparatus, and then the pressure in the chamber of said apparatus was controlled to 10⁻⁶ torr. Thereafter, an electric current was applied to the cell to evaporate the above introduced material, thereby forming a first hole injection layer having a thickness of 80 nm on the ITO substrate. HI-2 was then introduced into another cell of said vacuum vapor depositing apparatus, and evaporated by applying electric current to the cell, thereby forming a second hole injection layer having a thickness of 5 nm on the first hole injection layer. HT-1 was introduced into one cell of the vacuum vapor depositing apparatus, and evaporated by applying electric current to the cell, thereby forming a first hole transport layer having a thickness of 10 nm on the second hole injection layer. HT-3 was introduced into another cell of the vacuum vapor depositing apparatus, and evaporated by applying electric current to the cell, thereby forming a second hole transport layer having a thickness of 60 nm on the first hole transport layer. As a host material, a first host compound (H-1) and a second host compound (H2-41) were introduced into two cells of the vacuum vapor depositing apparatus, respectively. A dopant compound (D-71) was introduced into another cell. The two host materials were evaporated at a 1:1 rate, while the dopant was evaporated at a different rate from the host materials, so that the dopant was deposited in a doping amount of 3 wt % based on the total amount of the host and dopant to form a light-emitting layer having a thickness of 40 nm on the second hole transport layer. ET-1 and EI-1 were introduced into two cells of the vacuum vapor depositing apparatus, respectively, and evaporated at a 1:1 rate to form an electron transport layer having a thickness of 30 nm on the light-emitting layer. After depositing EI-1 as an electron injection layer having a thickness of 2 nm, an Al cathode having a thickness of 80 nm was then deposited by another vacuum vapor deposition apparatus on the electron injection layer to produce an OLED. The produced OLED showed a red emission having a luminance of 1,000 cd/m², and a current efficiency of 29.5 cd/A at a driving voltage of 3.5V. The minimum time taken to be reduced to 97% of the luminance at 5,000 nit was 114 hours.

[Device Example 2] OLED Using the Compound of the Present Disclosure

OLED was produced in the same manner as in Device Example 1, except that compound H-55 was used as a first host of the light-emitting material. The produced OLED showed a red emission having a luminance of 1,000 cd/m², and a current efficiency of 30.6 cd/A at a driving voltage of 3.6 V. The minimum time taken to be reduced to 97% of the luminance at 5,000 nit was 29 hours.

[Device Example 3] OLED Using the Compound of the Present Disclosure

OLED was produced in the same manner as in Device Example 1, except that compound H-56 was used as a first host of the light-emitting material. The produced OLED showed a red emission having a luminance of 1,000 cd/m², and a current efficiency of 29.2 cd/A at a driving voltage of 3.5 V. The minimum time taken to be reduced to 97% of the luminance at 5,000 nit was 12 hours.

[Device Example 4] OLED Using the Compound of the Present Disclosure

OLED was produced in the same manner as in Device Example 1, except that compound H-25 was used as a first host of the light-emitting material. The produced OLED showed a red emission having a luminance of 1,000 cd/m², and a current efficiency of 29.7 cd/A at a driving voltage of 3.5 V. The minimum time taken to be reduced to 97% of the luminance at 5,000 nit was 89 hours.

[Device Example 5] OLED Using the Compound of the Present Disclosure

OLED was produced in the same manner as in Device Example 1, except that compound H-66 was used as a first host of the light-emitting material. The produced OLED showed a red emission having a luminance of 1,000 cd/m², and a current efficiency of 29.9 cd/A at a driving voltage of 3.5 V. The minimum time taken to be reduced to 97% of the luminance at 5,000 nit was 167 hours.

[Device Example 6] OLED Using the Compound of the Present Disclosure

OLED was produced in the same manner as in Device Example 1, except that compound H-34 was used as a first host of the light-emitting material. The produced OLED showed a red emission having a luminance of 1,000 cd/m², and a current efficiency of 26.9 cd/A at a driving voltage of 3.4 V. The minimum time taken to be reduced to 97% of the luminance at 5,000 nit was 62 hours.

[Device Example 7] OLED Using the Compound of the Present Disclosure

OLED was produced in the same manner as in Device Example 1, except that compound H-34 and compound H2-528 were used as a first host and a second host of the light-emitting material, respectively. The produced OLED showed a red emission having a luminance of 1,000 cd/m², and a current efficiency of 30.0 cd/A at a driving voltage of 3.6 V. The minimum time taken to be reduced to 97% of the luminance at 5,000 nit was 58 hours.

[Device Example 8] OLED Using the Compound of the Present Disclosure

OLED was produced in the same manner as in Device Example 1, except that compound H-67 was used as a first host of the light-emitting material. The produced OLED showed a red emission having a luminance of 1,000 cd/m², and a current efficiency of 29.7 cd/A at a driving voltage of 3.5 V. The minimum time taken to be reduced to 97% of the luminance at 5,000 nit was 95 hours.

[Device Example 9] OLED Using the Compound of the Present Disclosure

OLED was produced in the same manner as in Device Example 1, except that compound H-35 was used as a first host of the light-emitting material. The produced OLED showed a red emission having a luminance of 1,000 cd/m², and a current efficiency of 28.6 cd/A at a driving voltage of 3.6 V. The minimum time taken to be reduced to 97% of the luminance at 5,000 nit was 95 hours.

[Device Example 10] OLED Using the Compound of the Present Disclosure

OLED was produced in the same manner as in Device Example 1, except that compound H-68 was used as a first host of the light-emitting material. The produced OLED showed a red emission having a luminance of 1,000 cd/m², and a current efficiency of 28.9 cd/A at a driving voltage of 3.6 V. The minimum time taken to be reduced to 97% of the luminance at 5,000 nit was 18 hours.

[Device Example 11] OLED Using the Compound of the Present Disclosure

OLED was produced in the same manner as in Device Example 1, except that a thickness of the first hole injection layer was 90 nm; compound H-1 was used to form the second hole transport layer instead of HT-3; compound H2-41 was used as a single host for the light-emitting layer; dopant compound D-71 was deposited in a doping amount of 2 wt % based on the total amount of the host and dopant; and a thickness of the electron transport layer was 35 nm. The produced OLED showed a red emission having a luminance of 1,000 cd/m², and a current efficiency of 27.2 cd/A at a driving voltage of 4.4 V.

[Device Example 12] OLED Using the Compound of the Present Disclosure

OLED was produced in the same manner as in Device Example 11, except that compound H-55 was used to form the second hole transport layer. The produced OLED showed a red emission having a luminance of 1,000 cd/m², and a current efficiency of 23.4 cd/A at a driving voltage of 3.8 V.

[Device Example 13] OLED Using the Compound of the Present Disclosure

OLED was produced in the same manner as in Device Example 11, except that compound H-56 was used to form the second hole transport layer. The produced OLED showed a red emission having a luminance of 1,000 cd/m², and a current efficiency of 23.3 cd/A at a driving voltage of 3.7 V.

[Device Example 14] OLED Using the Compound of the Present Disclosure

OLED was produced in the same manner as in Device Example 11, except that compound H-34 was used to form the second hole transport layer. The produced OLED showed a red emission having a luminance of 1,000 cd/m², and a current efficiency of 26.9 cd/A at a driving voltage of 4.2 V.

[Device Example 15] OLED Using the Compound of the Present Disclosure

OLED was produced in the same manner as in Device Example 11, except that compound H-67 was used to form the second hole transport layer. The produced OLED showed a red emission having a luminance of 1,000 cd/m², and a current efficiency of 27.1 cd/A at a driving voltage of 4.5 V.

[Device Example 16] OLED Using the Compound of the Present Disclosure

OLED was produced in the same manner as in Device Example 11, except that compound H-35 was used to form the second hole transport layer. The produced OLED showed a red emission having a luminance of 1,000 cd/m², and a current efficiency of 25.5 cd/A at a driving voltage of 3.6 V.

[Device Example 17] OLED Using the Compound of the Present Disclosure

OLED was produced in the same manner as in Device Example 11, except that compound H-68 was used to form the second hole transport layer. The produced OLED showed a red emission having a luminance of 1,000 cd/m², and a current efficiency of 26.9 cd/A at a driving voltage of 3.8 V.

[Comparative Example 1] OLED Using a Conventional Compound

OLED was produced in the same manner as in Device Example 1, except that compound 1 as shown below was used as a first host of the light-emitting material. The produced OLED showed a red emission having a luminance of 1,000 cd/m², and a current efficiency of 0.6 cd/A at a driving voltage of 7.8 V. Due to the low efficiency, lifespan cannot be measured.

[Comparative Example 2] OLED Using a Conventional Compound

OLED was produced in the same manner as in Device Example 11, except that compound 1 as shown above was used to form the second hole transport layer. The produced OLED showed a red emission having a luminance of 1,000 cd/m², and a current efficiency of 10.2 cd/A at a driving voltage of 5.5 V.

The organic electroluminescent compounds of the present invention provide better luminous efficiency and longer lifespan than the conventional organic electroluminescent compounds. The device employing the organic electroluminescent compound of the present invention exhibits excellent luminous efficiency, in particular, excellent current/power efficiencies. 

1. An organic electroluminescent compound represented by the following formula 1:

wherein L represents a single bond, or a substituted or unsubstituted (C6-C30)arylene; X represents —O—, —S—, —CR₁₁R₁₂—, or —NR₁₃—; R₁₁ and R₁₂, each independently, represent a substituted or unsubstituted (C1-C30)alkyl, a substituted or unsubstituted (C6-C30)aryl, or a substituted or unsubstituted 5- to 30-membered heteroaryl, or may be linked to an adjacent substituent(s) to form a substituted or unsubstituted, (C3-C30), mono- or polycyclic, alicyclic or aromatic ring, whose carbon atom(s) may be replaced with at least one hetero atom selected from nitrogen, oxygen and sulfur; R₁₃ represents a substituted or unsubstituted (C6-C30)aryl, or a substituted or unsubstituted 5- to 30-membered heteroaryl; R₁ to R₄, each independently, represent hydrogen, deuterium, a halogen, a cyano, a substituted or unsubstituted (C1-C30)alkyl, a substituted or unsubstituted (C6-C30)aryl, a substituted or unsubstituted 5- to 30-membered heteroaryl, a substituted or unsubstituted (C3-C30)cycloalkyl, a substituted or unsubstituted (C1-C30)alkoxy, a substituted or unsubstituted tri(C1-C30)alkylsilyl, a substituted or unsubstituted di(C1-C30)alkyl(C6-C30)arylsilyl, a substituted or unsubstituted (C1-C30)alkyldi(C6-C30)arylsilyl, a substituted or unsubstituted tri(C6-C30)arylsilyl, a substituted or unsubstituted mono- or di-(C1-C30)alkylamino, a substituted or unsubstituted mono- or di-(C6-C30)arylamino, or a substituted or unsubstituted (C1-C30)alkyl(C6-C30)arylamino; R₁ and R₄, each independently, may be linked to an adjacent substituent(s) to form a substituted or unsubstituted, (C3-C30), mono- or polycyclic, alicyclic or aromatic ring, whose carbon atom(s) may be replaced with at least one hetero atom selected from nitrogen, oxygen and sulfur; a represents an integer of 0 to 4; where a is 2 or more, each of R₁ may be the same or different; b and c, each independently, represent an integer of 0 to 6; where b or c is 2 or more, each of R₂ or R₃ may be the same or different; d represents an integer of 0 to 3; where d is 2 or more, each of R₄ may be the same or different; e represents 0 or 1; provided that where e is 0, b+c=1 or more, and at least one of R₂ and R₃ represents a substituted or unsubstituted 5- to 30-membered heteroaryl; and the heteroaryl contains at least one hetero atom selected from B, N, O, S, Si, and P.
 2. The organic electroluminescent compound according to claim 1, wherein the substituents of the substituted alkyl, the substituted aryl, the substituted heteroaryl, the substituted cycloalkyl, the substituted alkoxy, the substituted trialkylsilyl, the substituted dialkylarylsilyl, the substituted alkyldiarylsilyl, the substituted triarylsilyl, the substituted mono- or di-alkylamino, the substituted mono- or di-arylamino and the substituted alkylarylamino in L, R₁ to R₄, and R₁₁ to R₁₃, each independently, are at least one selected from the group consisting of deuterium, a halogen, a cyano, a carboxy, a nitro, a hydroxy, a (C1-C30)alkyl, a halo(C1-C30)alkyl, a (C2-C30)alkenyl, a (C2-C30)alkynyl, a (C1-C30)alkoxy, a (C1-C30)alkylthio, a (C3-C30)cycloalkyl, a (C3-C30)cycloalkenyl, a 3- to 7-membered heterocycloalkyl, a (C6-C30)aryloxy, a (C6-C30)arylthio, a 5- to 30-membered heteroaryl unsubstituted or substituted with a (C6-C30)aryl, a (C6-C30)aryl unsubstituted or substituted with a 5- to 30-membered heteroaryl, a tri(C1-C30)alkylsilyl, a tri(C6-C30)arylsilyl, a di(C1-C30)alkyl(C6-C30)arylsilyl, a (C1-C30)alkyldi(C6-C30)arylsilyl, an amino, a mono- or di-(C1-C30)alkylamino, a mono- or di-(C6-C30)arylamino, a (C1-C30)alkyl(C6-C30)arylamino, a (C1-C30)alkylcarbonyl, a (C1-C30)alkoxycarbonyl, a (C6-C30)arylcarbonyl, a di(C6-C30)arylboronyl, a di(C1-C30)alkylboronyl, a (C1-C30)alkyl(C6-C30)arylboronyl, a (C6-C30)aryl(C1-C30)alkyl, and a (C1-C30)alkyl(C6-C30)aryl.
 3. The organic electroluminescent compound according to claim 1, wherein L represents a single bond, or a substituted or unsubstituted (C6-C20)arylene; X represents —O—, —S—, —CR₁₁R₁₂—, or —NR₁₃—; R₁₁ and R₁₂, each independently, represent a substituted or unsubstituted (C1-C20)alkyl, or a substituted or unsubstituted (C6-C20)aryl, or may be linked to each other to form a substituted or unsubstituted (C3-C20), mono- or polycyclic aromatic ring; R₁₃ represents a substituted or unsubstituted (C6-C20)aryl; R₁ and R₄, each independently, represent hydrogen, a substituted or unsubstituted (C1-C20)alkyl, a substituted or unsubstituted (C6-C20)aryl, or a substituted or unsubstituted 5- to 20-membered heteroaryl, or may be linked to an adjacent substituent(s) to form a substituted or unsubstituted, (C3-C20), mono- or polycyclic aromatic ring; R₂ and R₃, each independently, represent hydrogen, a substituted or unsubstituted (C1-C20)alkyl, a substituted or unsubstituted (C6-C20)aryl, or a substituted or unsubstituted 5- to 20-membered heteroaryl; provided that where e is 0, b+c=1 or more, and at least one of R₂ and R₃ represents a substituted or unsubstituted 13- to 25-membered heteroaryl; and the heteroaryl contains at least one hetero atom selected from N, O, and S.
 4. The organic electroluminescent compound according to claim 1, wherein e represents 1; X represents —O—, —S—, or —NR₁₃—; R₁₃ represents a substituted or unsubstituted phenyl, a substituted or unsubstituted naphthyl, a substituted or unsubstituted biphenyl, a substituted or unsubstituted phenyl-naphthyl, a substituted or unsubstituted naphthyl-phenyl, a substituted or unsubstituted anthracenyl, a substituted or unsubstituted phenanthrenyl, a substituted or unsubstituted terphenyl, a substituted or unsubstituted tetracenyl, a substituted or unsubstituted chrysenyl, a substituted or unsubstituted pyrenyl, a substituted or unsubstituted triphenylenyl, or a substituted or unsubstituted fluoranthenyl; and R₁ and R₄, each independently, represent hydrogen, a substituted or unsubstituted phenyl, a substituted or unsubstituted biphenyl, or a substituted or unsubstituted naphthyl, or may be linked to an adjacent substituent(s) to form a substituted or unsubstituted benzene or naphthalene ring.
 5. The organic electroluminescent compound according to claim 1, wherein e represents 0; b+c=1 or more; L represents a substituted or unsubstituted (C6-C20)arylene; and at least one of R₂ and R₃ is selected from the following formulae 2-1 to 2-3.

wherein L_(a), L_(b), and L_(c), each independently, represent a single bond, or a substituted or unsubstituted (C6-C30)arylene; Z represents —S—, —O—, —NR₂₃—, or —CR₂₄R₂₅—; R₂₀, and R₂₃ to R₂₅, each independently, represent a substituted or unsubstituted (C1-C30)alkyl, a substituted or unsubstituted (C6-C30)aryl, or a substituted or unsubstituted 3- to 30-membered heteroaryl, or may be linked to an adjacent substituent(s) to form a substituted or unsubstituted, (C3-C30), mono- or polycyclic, alicyclic or aromatic ring, whose carbon atom(s) may be replaced with at least one hetero atom selected from nitrogen, oxygen and sulfur; R₁₄ to R₁₉, each independently, represent hydrogen, deuterium, a halogen, a cyano, a substituted or unsubstituted (C1-C30)alkyl, a substituted or unsubstituted (C3-C30)cycloalkyl, a substituted or unsubstituted (C6-C30)aryl, a substituted or unsubstituted 3- to 30-membered heteroaryl, a substituted or unsubstituted tri(C1-C30)alkylsilyl, a substituted or unsubstituted tri(C6-C30)arylsilyl, a substituted or unsubstituted di(C1-C30)alkyl(C6-C30)arylsilyl, a substituted or unsubstituted (C1-C30)alkyldi(C6-C30)arylsilyl, a substituted or unsubstituted mono- or di-(C1-C30)alkylamino, a substituted or unsubstituted mono- or di-(C6-C30)arylamino, or a substituted or unsubstituted (C1-C30)alkyl(C6-C30)arylamino, or may be linked to an adjacent substituent(s) to form a substituted or unsubstituted, (C3-C30), mono- or polycyclic, alicyclic or aromatic ring, whose carbon atom(s) may be replaced with at least one hetero atom selected from nitrogen, oxygen and sulfur; f represents an integer of 0 to 3; g, h, i, and k, each independently, represent an integer of 0 to 4; j represents an integer of 0 to 5; where f, g, h, i, j or k is 2 or more, each of R₁₄, R₁₅, R₁₆, R₁₇, R₁₈, or R₁₉ may be the same or different; the heteroaryl contains at least one hetero atom selected from N, O, and S; and * represents a bonding site.
 6. The organic electroluminescent compound according to claim 1, wherein the compound represented by formula 1 is selected from the group consisting of:


7. An organic electroluminescent material comprising the organic electroluminescent compound according to claim
 1. 8. An organic electroluminescent device comprising the organic electroluminescent compound according to claim
 1. 